Acero inoxidable 316L - Resistente a la corrosión

Aplicaciones de soldadura pesada

In general, stainless steel is susceptible to intergranular corrosion due to the precipitation of chromium carbides between the grains during welding. It can also occur when carbon diffuses into the body of stainless steel from oil, plastic tape, and other organic substances under heat. The process is known as carburization. However, due to low carbon content, 316L thrives under such environments by offering excellent resistance to intergranular corrosion. Therefore, fabricators choose 316L over 316 in heavy gauge (>6 mm) componentes soldados.

 

Aquí hay una tabla comparativa concisa del acero inoxidable 316L con otros tipos comunes de acero inoxidable:

Tipo de acero inoxidable	Resistencia a la corrosión	Resistencia a la tracción	Componentes químicos principales	Costo típico	Aplicaciones típicas
316L	muy alto	Alto	16-18 % Cr, 10-14 % Ni, 2-3 % Mo,<0.03% C	Moderado	Dispositivos médicos, entornos marinos, procesamiento químico.
304	Alto	Moderado	18-20% Cr, 8-12% Ni,<0.08% C	Más bajo	Equipamiento de cocina, paneles arquitectónicos.
410	Moderado	Alto	11,5-13,5 % cromo,<0.15% C	Más bajo	Cubiertos, palas de turbinas de vapor y gas.
321	Alto	Alto	17-19% Cr, 9-12% Ni, 5x%C Ti	Más alto	Componentes aeroespaciales, sistemas de escape.